WALL SC 605-C

DEFINITION

Epoxy top layer paint with two components, without solvent for vertical surfaces

USAGE AREAS

It is an Epoxy top layer paint with two components, without solvent for vertical surfaces with high mechanical endurance and wear resistance, easy to clean and can be used in factories, assembly workshops, depots, aircraft hangers, store, auto-park, food facilities, water tanks, hospitals, chemical and drug industry, energy power plants, in units where hygiene is desired, on surfaces where plaster has been applied and all industrial areas .

 

Type                                                      

TS EN 1504-2/ April 2008 Principle 5(PR): 5,1 Physical Resistance / Surface Improvement Coating Application ( C )

Color

RAL colors

Appearance

Bright

Solid Matter By Weight, %

95

Density

1,55 g/cm³

Waste

0,200-0,500 kg/m²

Package

20 kg A Component + 4 kg B Component: Total 24 kg

Flash Point

>25 °C

Mixture Ratio

5 / 1

Application Methods

Brush, Roller, Airless Gun,

Mixture Life

30 minutes/  25°C

Shelf Life

1 year

Waiting Time Between Coating

12 hours/  25°C

Drying Time

12 hours /  25°C

Mechanical strength

7 days

Shore D Hardness

Fire Reaction Class

70 (7 days / 25°C)

C

Equipment Cleaning

Epoxy Thinner

SURFACE PREPARATION 

* The surfaces to be applied should be clear of grease, dust and dirt.

* Free particles on surfaces, cement slurry on cement surfaces and parts that prevent gluing should be cleared.

* Yüzeydeki serbest parçalar, beton yüzeylerdeki çimento şerbeti ve 
yapışmaya engel olan parçalar temizlenmelidir. 

MIXTURE PREPARATION
The components A and B should be mixed for at least 3-4 minutes with the aid of a low speed mixer until a homogeneous mixture is obtained, taking into account the mixing ratios. It is ready for application after mixing

COATING SYSTEM
The concrete surface where application would be done should be primed using SC 210 multi-purpose Epoxy Primer, SC 215 Epoxy Primer without Solvent or SC 270 Low Viscosity Epoxy Impregnated Primer. On moist surfaces SC 220 should be used and on 100% moist surfaces Epoxy Primer. 12 hours after the priming process, epoxy painting process can start. In brush or roller applications, epoxy brush or roller should be used. If it is necessary, the product itself can also be used as the first layer primer. In applications over plaster, prior to using SC 605 Epoxy Top Layer Pint without solvent, water based acrylic BRV Primer 405 should be applied as transition primer. In cases where high UV durability is desired, it is suggested to apply P125 protective coating with 0,150 – 0,200 kg/m² waste.

APPLICATION CONDITIONS

* The surfaces must have sufficient endurance. Concrete should endure minimum 25 N/mm² pressure and endure against at least 1,5-2 N/mm² pull-off strength.

* The surface should be clean, straight, dry and should not exceed 5% moisture and if moisture is above this rate, SC 220 should be used on moist surfaces and Epoxy Primer on 100% moist surfaces.

* The priming should have completed its curing prior to moving on to the top layer epoxy painting process.

* Application should be avoided under 10°C and in high moisture environments.

* The mixture ratios should be paid attention to.

Products suggested to be used under this product :

* SC 210 Multi-purpose Epoxy Primer * SC 270 Epoxy adhesion bridge Low Viscosity Impregnated Primer