PRIMER AC 070

DEFINITION

Two-component, solvented epoxy primer containing anticorrosive zinc dust.

USAGE AREAS
In particular, iron, which is in contact with water and humid and provides long-term resistance to rust by making cathodic protection on steel surfaces.

Type	TS EN ISO 12944-5
Colour	Gray
Outlook	Mat
Thinner	Epoxy Thinner
Solid Matter by Weight, %	76
Density	1,90 g/cm³
Waste	For 40 micron at single coat 100 gr/m²
Package	27 kg A Component + 3 kg B Component: Total 30 kg
Flash Point	>25 °C
Mixture Ratio	9 / 1
Application Methods	Brush, Roller, Air Gun, Airless Gun
Mixture Life	1 hours / 25°C
Shelf Life	1 year
Waiting Time Between Coats	6 hours / 25 °C
Drying Time	12 hours / 25 °C
Mechanical Strength	7 days
Equipment Cleaning	Epoxy Thinner

SURFACE PREPARATION

* The surfaces to be applied must be free from oil, dust, and dirty. . It is especially recommended to sandblast at least Sa 2½ degree according to Swedish standard SIS 05 59 00 for surface cleaning. The first coat of primer is applied immediately after sandblasting.

MIXING PREPARATION

A and B component should be mixed with a low speed mixer for at least 3-4 minutes until a homogenous mixture is obtained by paying attention to mixture ratios. It is ready for application after mixing .

COATING SYSTEM

In application with primer prepared, bolt heads, welding seams and sharp edges should be taken care of. Paint should be applied to metal surfaces as one or two coats with a total dry film thickness of 30-35 microns.

APPLICATION CONDITIONS

Avoid application in very humid environments and below 10°C. Products that can be used upper this product : - AC 976 Solvented Epoxy Coal Tar Top Coat Paint - AC 2480 Epoxy Intermediate Coat Primer - AC 6380 Epoxy Top Coat Paint - AC 6490 Epoxy Top Coat Paint