SC 650 ST

DEFINITION

İTwo component, solvent free, epoxy, self leveling floor coating..

Public Works Pos. No: 04.379/H03

USAGE AREAS

It is used in all industrial floors in hygienic units, in factories, installation workshops, warehouses, aircraft hangars, shops, parking, food facilities, hospitals, chemistry and medicine industry. It is used as a self leveling solvent free epoxy floor coating on the last layer of the multilayer system or on its own with high mechanical strength and high abrasion resistance, easy to clean


Type

TS EN 1504-2/ April 2008 Principle 5 (PR): 5.1 Physical Resistance / Surface Improvement Coating Application (C)

Colour

RAL colours

Outlook

Bright

Solid Matter by Weight, %

98

Density

A+B; 1,40 g/cm³

A+B+C; 1,80 g/cm³

Waste

A+B; for 250 micron dry film thickness  0,350 kg/m2

        For 1 mm dry film thickness   1,400 kg/m2

A+B+C; for 1 mm dry film thickness  1,800 kg/m2

Package

A+B; 20 kg A Component + 4 kg B Component : Total 24 kg

A+B+C; 20 kg A Component + 4 kg B Component + 12,5 kg C Component:    Total 36,5 kg

C Component 25 kg in Kraft Bag packaging

Flash Point

>25 °C

Mixture Ratio

5 / 1

Application Methods

Brush, Roller, Airless Gun, Trowel

Mixture Life

30 minutes /  25°C

Shelf Life

1 year

Waiting Time Between Coats

12 hours /  25°C

Drying Time

12 hours /  25°C

Mechanical Strength

7 days

Adhesion Strength (TS EN ISO 1542)

>2 N/mm2

Shore D Hardnes (EN ISO 868)

75±3 /23 °C

Pressure Resistance (TS EN 12190)

80 N/mm2

Bending Strength   (TS EN 12190)

45 N/mm2

Tensile Strength (DIN 53504)

20 N/mm2

Fire Reaction Class

Cfl

Equipment Cleaning

7 days /23°C

* Surface should have sufficient strength. The concrete has a compression strength of at least 25 N/mm², nd a tensile strength of at least 1,5-2 N/mm².

* The surface must be clean and dry. Humidity must not exceed 5%, If the humidity is above this ratio, SC 220 100% Epoxy Primer for humid surfaces used on humid surfaces should be preferred.

* The primer must have been completed its curing before the top coat application is started.

* Avoid application in very humid environments and below 10°C.

* Mixing ratios should be considered.

COATING SYSTEM

Floor coating with roll:

* Primer : 1 coat PRIMER SC 215 Solvent Free Epoxy Prime

* Coating : 2 coats SC 650/ST Solvent Free Epoxy Coating

Wall and ceiling coating with roll:

* Primer : 1 coat PRIMER SC 215 Solvent Free Epoxy Prime

* Coating : 2 coats SC 650-ST Solvent Free Epoxy Coating Thickener (Silica 1) is added in the standard product up to 0.5% of the total mixture.

Self leveling coating 1 mm:

* Primer : 1 coat PRIMER SC 215 Solvent Free Epoxy Prime

* Top Coat Coating : 1 coat SC 650-ST Solvent Free Epoxy Coating

Self leveling coating 1,5-3,0 mm :

* Primer r : 1 coat PRIMER SC 215 Solvent Free Epoxy Prime

* Coating : 1 coat SC 650-ST Solvent Free Epoxy Coating + 0,1-0,3 mm Quarz

For high decorative looks:

* Primer : 1 coat PRIMER SC 215 Solvent Free Epoxy Prime

* Coating : 1 coat SC 650-ST Solvent Free Epoxy Coating + 0,1-0,3 Quarz with mineral filler

Orange patterned textured coating:

* Primer : 1 coat PRIMER SC 215 Solvent Free Epoxy Prime

* Inter Coat Coating: 1 coat SC 650-ST Solvent Free Epoxy Coating

* Orange patterned topcoat: :

1 coat SC 650-ST Solvent Free Epoxy Coating Thickener (Silica 1) is added in the standard product up to 0.5% of the total mixture.

When high UV resistance is desired:

* PU 125 protective coating is recommended as topcoat.

 

Before preparing the mixture component A should be mixed with a low-speed mixer (300-400 rpm) until the product is completely homogeneous, B-Component must be completely poured into Component A taking care of mixture ratio and the product should be mixed for at least 2 minutes until homogeneous. Thickener (Silica 1) is added in the prepared SC 650-ST standard product up to 0.5% of the total mixture and the product should be ready for application by mixing for coating of walls and ceilings to be applied with rolls.

Thickener (Silica 1) is added in the prepared SC 650-ST standard product up to 0.5% of the total mixture and the product should be ready for application by mixing for orange patterned textured coating application.

Floor coating with roll:

* Primer                   : 1 coat PRIMER SC 215 Solvent Free Epoxy Prime

* Coating             : 2 coats SC 650/ST Solvent Free Epoxy Coating

Wall and ceiling coating with roll:

* Primer                    : 1 coat PRIMER SC 215 Solvent Free Epoxy Prime

* Coating               : 2 coats SC 650-ST Solvent Free Epoxy Coating Thickener (Silica 1) is added in the standard product up to 0.5% of the total mixture.

Self leveling coating 1 mm:

* Primer                     : 1 coat PRIMER SC 215 Solvent Free Epoxy Prime

* Top Coat Coating  : 1 coat SC 650-ST Solvent Free Epoxy Coating

Self leveling coating 1,5-3,0 mm :

* Primer r                     : 1 coat PRIMER SC 215 Solvent Free Epoxy Prime

* Coating               : 1 coat SC 650-ST Solvent Free Epoxy Coating + 0,1-0,3 mm Quarz

For high decorative looks:

* Primer                     : 1 coat PRIMER SC 215 Solvent Free Epoxy Prime

* Coating               : 1 coat  SC 650-ST Solvent Free Epoxy Coating + 0,1-0,3 Quarz with mineral filler

Orange patterned textured coating:

* Primer                     :  1  coat PRIMER SC 215 Solvent Free Epoxy Prime

* Inter Coat Coating:  1  coat SC 650-ST Solvent Free Epoxy Coating

* Orange patterned topcoat: :1 coat SC 650-ST Solvent Free Epoxy Coating Thickener (Silica 1) is added in the standard product up to 0.5% of the total mixture.

When high UV resistance is desired:

* PU 125 protective coating is recommended as topcoat.

Application system

Product

Waste

Roll coating

-Primer coat SC 215

-2 coats SC 650-ST

0,250-0,500 kg/m2

0,250-0,300 kg/m2  for every coat

Wall and ceiling coating with roll

- Primer coat SC 215

-2 coats SC 650-ST (thickener silica 1"  is added in the standard product Up to 5% of the total amount of mixture.)  

0,250-0,500 kg/m2

0,250-0,300 kg/m2 for every coat

Self leveling coating 1 mm

- Primer coat SC 215

-1st part SC 650-ST + 0,5 part 0,1-0,3 Quarz sand

0,250-0,500 kg/m2

1,800 kg/m2   for 1mm thickness               

Self leveling coating 1,5-3,0 mm  

- Primer coat SC 215

-1 part SC 650/ST + 1 part 0,1-0,3 Quarz sand       

0,250-0,500 kg/m2

3,000  kg/m2 for 1,5 mm thickness

6,000 kg/m2 for 1mm thicknes3s

Orange patterned textured coating

- Primer coat SC 215

-1st coat  SC 650-ST

-2nd coat SC 650-ST (thickener silica 1"  is added in the standard product Up to 5% of the total amount of mixture. )                                        

0,250-0,500 kg/m2

0,400-0,500 kg/m2

0,500-0,700 kg/m2

When high UV resistance is desired

-Top coat PU 125

0,150-0,200 kg/m2


2163

BRV Epoxy & Polyurethane Systems Inc.

A.O.S.B. 10010 Sokak No:7 Çiğli/İZMİR

12

2163-CPD-0118

EN 1504-2:2004

Principle 5 (PR): Physical Resistance / Surface Improvement

5.1 Coating Application ( C )

Specifications

Values

Resistance to impact

CLASS  II  ≥10Nm

Adhesive strength by pull-off

≥2 N/mm2 (Rijit Sistem)

Resistance to Wear  (Taber) (Wheel Class :H 22 ,

Wheel Load: 1000gr ,

Cycle : 1000 cycle)

<3000 mg

Capillary Water Absorption and Water Permeability

<0.1 kg/m2.h0.5

Fire Reaction Class

Cfl

 