PRIMER SC 215

DEFINITION

two component low viscosity solvent free epoxy primer

Public Works Pos. No: 04.379/H02

USAGE AREAS

It is used on factory and warehouse floors, working areas, loading zones, industrial floors exposed to medium and heavy loads, concrete surfaces, cement mortars and screed surfaces, normal and highly absorbent surfaces, for filling fine pores and cracks and capillary spaces on epoxy based mortars or prior to application of epoxy, polyurethane, polyurea topcoats.

Type

TS EN 1504-2/ April 2008 Principle 5(PR): 5.1 Physical Resistance / Surface Improvement Coating Application C

Colour

Colourless

Outlook

Transparent

Solid Matter by Weight, %

100

Density ( A Component)

               ( B Component )

               (A+B Mixture density)

1,10 gr/cm³

  1. gr/cm³

1.08 gr/cm³

Waste

0,300 – 0,500 kg / m2

Package

14 kg A Component + 7 kg B Component = Total 21 kg

Flash Point

>25 °C

Mixture Ratio

2 / 1

Application Methods

Brush, Roller, Trowell, Airless Gun

Mixture Life (Pot life)

30 minutes / 25°C

Shelf Life

1 year

Waiting Time Between Coats

12 hours / 25°C

Drying Time

12 hours / 25°C

Mechanical Strength

Pressure Resistance (EN 196-1)

Bending Strength (EN 196-1)

Adhesion Strength (EN 4624)

Shore D Hardness (DIN 53505)

7days

95 N/mm²

30 N/mm²

>1.5 N/mm²

83 (%50 Relative humidity / 23 ºC  7days)

Equipment Cleaning

Epoxy Thinner

SURFACE PREPARATION

Free particles and paint residues on the surface must be thoroughly cleaned, brokens and cracks must be repaired, surfaces should be roughened mechanically (blastrack or milling router) and cleaned from vacuum with vacuum cleaner

MIXING PREPARATION

A and B component should be mixed with a low speed mixer for at least 3-4 minutes until a homogenous mixture is obtained by paying attention to mixture ratios. It is ready for application after mixing.

APPLICATION CONDITIONS

* Surface should have sufficient strength. The concrete should have a compressive strength of at least 25 N/mm² and a tensile strength of at least 1,5 N/mm².

* Surfaces must be clean, smooth and dry. Humid is not pass 5%. If the humidity is above this ratio, SC 220 Epoxy Prime for Humid Surfaces should be preferred.

* The SC 215 should be completed its curing before the top coat coating is started.

* Avoid application in very humid environments and below 5°C.

* Mixing ratios should be considered. Products that can be used upper this product :

* SC 650 ST Solvent Free Epoxy Resin Based Top Coat Coating

* SC 605 Epoxy Top Coat Paint for Vertical Surfaces

* SC 645 Orange Coat Patterned Top Coat Epoxy Coating

* SC 800 Hygienic Epoxy Top Coat Coating and Paint for Potable Water Reservoir a

* SC 902 Solvent Free Epoxy Top Coat Coating.

* SC 905 Solvent Free Epoxy Paint Resistant to Chemical Matter for Vertical Surfaces

* SC 950 Solvent Free Epoxy Coating Resistant to Chemical Matter

* SC 1200 Modular Container Epoxy Floor Coating

* PU 145 Polyurethane Self Leveling Coating

* PU 150 Polyurethane Semi-Elastic Self Leveling Coating

* PU 160 Polyurethane Elastic Water Isolation Membrane

* PU 170 Polyurethane Water Isolation Membrane