SURFACE PREPARATION

* The surfaces to be applied must be free from oil, dust, and dirty.

* Free parts on the surface, cement grout on concrete surfaces and parts that prevent adhesion must be cleaned.

MIXING PREPARATION

A and B component should be mixed with a low speed mixer for at least 3-4 minutes until a homogenous mixture is obtained by paying attention to mixture ratios. It is ready for application after mixing.

COATING SYSTEM

If the floor is precast concrete panel, depending on the surface suction power, the SC 200-K Condensed Intermediate Primer is applied at 0.300-0.800 kg /m². If the floor is sheet metal, anticorrosive primer must be used. The minimum dry film thickness of these primers should be 100 microns. Also, the cleaning of the sheets must be at SA 2½ ranks

APPLICATION CONDITIONS

* Surface should have sufficient strength

* The surface must be clean and dry. Humidity must not exceed 5%, If the humidity is above this ratio, SC 220 100% Epoxy Primer for humid surfaces used on humid surfaces should be preferred.

* Surface should have sufficient strength

* The surface must be clean and dry. Humidity must not exceed 5%, If the humidity is above this ratio, SC 220 100% Epoxy Primer for humid surfaces used on humid surfaces should be preferred.

* The primer to be used must have been completed its curing before the top coat coating is started.

* Avoid application in very humid environments and below 10°C.

* Mixing ratios should be considered.

Products that can be used under this product:

* SC 210 Multipurpose Epoxy Primer

* SC 200-K Condensed Intermediate Coat Primer

* SC 220 Epoxy Primer for 100% Humidy Surfaces

* SC 270 Epoxy Impregnating Primer with Low Viscosity

* AC 2480 Epoxy Intermediate Coat Primer

* AC 070 Epoxy Zinc Rich Primer