EPOKSİ ÜRÜNLER
-
Floor Coatings
- PRIMER WG 032
- WALL WG 034
- BRV SC 105
- BRV SC-200 K
- PRIMER SC 210
- PRIMER SC 215
- PRIMER SC 220
- SC Z-230
- PRIMER SC 270
- PRIMER SC 325
- DECOFLOOR SC 330
- FLOOR SC 470
- SC 600
- WALL SC 605
- WALL SC 605-C
- BRV SC 610 SOLVENTSİZ EPOKSİ SON KAT BOYA-ENG
- BRV SC 620 SOLVENTSİZ TEKSTÜRLÜ EPOKSİ SON KAT BOYA-E
- BRV SC 625 SOLVENTSİZ EPOKSİ SON KAT KAYMAZ ZEMİN BOYASI-E
- FLOOR SC 645
- SC 650 ST
- FLOOR SC 902
- FLOOR SC 903
- BRV SC 905 • DÜŞEY YÜZEYLER İÇİN KİMYASAL MADDELERE DAYANIKLI SOLVENTSİZ EPOKSİ SON KAT BOYA
- FLOOR SC 950
- FLOOR SC 1200
- FLOOR AC 6380
- ROAD AC 6388
- Waterproofing Products
- Repair Anchorage and Assembly Products
- Joint Filler and Ceramic Adhesive Products
- Wood Protection Adhesive and Lamination Products
- Natural Stone Protectors
- Water Reservoir & Drainpipe Insulation Products
- Anticorrosive Products For Metal Surfaces
- Thinners
-
Floor Coatings
-
POLIURETAN PRODUCTS
- ZEMIN KAPLAMA ve BOYAMA URUNLERI
- SU YALITIM URUNLERI
- YAPISAL GUCLENDIRME TAMIR ANKRAJ MONTAJ URUNLERI
- AHSAP KORUYUCU, YAPISTIRICI ve LAMINASYON URUNLERI
- DOGALTAS KORUYUCU URUNLER
- METAL YUZEYLER ICIN ANTIKOROZIF URUNLER
- Concrete Protection and Shining Products
- TINERLER
-
AKRILIK PRODUCTS
- SU YALITIM URUNLERI
- ZEMIN KAPLAMA ve BOYAMA URUNLERI
- Indoor & Outdoor Insulation and Painting
- Fire Retardant Insulation Paint
SEAL SC 2000
DEFINITION
Two component, solvent free epoxy, coal tar modified liquid insulation membrane
USAGE AREAS
It pastes concrete together by entering between cracks formed in concrete, basement, groundworks, pond, pier, bridge feet, foseptic isolation, foundation of buildings.When it is applied on the supporting columns and the curtain concrete of the buildings, it prevents that floor waters penetrates to concrete so it prevents both the corrosion of the concrete and the corrosion of the iron in the concrete. It is not affected by internal and external pressures, it does not separate from the surface, it reacts with the concrete and becomes an integral part of the concrete. On concrete floors of oil storage tanks, it is used with purpose to prevent oil from mixing with soil, it is resistant to salt water. Resistance to chemical substances is high.
Type | TS 11589 |
Colour | Dark Brown |
Outlook | Matt |
Solid Matter by Weight, % | 100 |
Density | 1,40 g/cm³ |
Waste | 0,500-1,500 kg / m2 |
Package | 16 kg A Component + 8 kg B Component:Tottal 24 kg |
Flash Point | >25 °C |
Mixture Ratio | 2 / 1 |
Application Methods | Brush, Roller, Trowell, Airless Gun |
Mixture Life | 30 min / 25°C |
Shelf Life | 1 year |
Waiting Time Between Coats | 12 hours / 25°C |
Drying Time | 12 hours / 25°C |
Mechanical Strength | 7 days |
Equipment Cleaning | Epoxy Thinner |
* The surfaces to be applied must be free from oil, dust, and dirty. Free parts on the surface, cement grout on concrete surfaces and parts that prevent adhesion must be cleaned.
MIXING PREPARATION
A and B component should be mixed with a low speed mixer for at least 3-4 minutes until a homogenous mixture is obtained by paying attention to mixture ratios. It is ready for application after mixing.
COATING SYSTEM
Prepared homogeneous mixture must be thoroughly poured onto the surface with roller or a suitable brush and it is applied to close the pores. If desired, it can be applied with air and airless gun. Carrier fiber application is recommended where water pressure is high. 7 days after it becomes resistant to chemicals. Screed, concrete, ceramic tile etc. can be easily laid on it. Before Seal SC 2000 epoxy coal tar modified liquid insulation membrane must completes its curing before top coat coating is started.
APPLICATION CONDITIONS
* Surface should have sufficient strength. The concrete should have a compressive strength of at least 25 N/mm² and a tensile strength of at least 1,5 – 2 N/mm².
* Surfaces must be clean, smooth and dry. Humid is not pass 5%. If the humidity is above this ratio, SC 220 Epoxy Prime for Humid Surfaces should be preferred.
* Before Seal SC 2000 epoxy coal tar modified liquid insulation membrane is started, SC 220 Epoxy Primer for 100% Humid Surfaces must completes its curing..
* Avoid application in very humid environments and below 10°C.
* Mixing ratios should be considered.