PRIMER SC 092

DEFINITION

Two component, low viscosity, epoxy wood adhesion bridge..

USAGE AREAS

It is used as bonding bridge in bonding processes to wood, bonding of wood to concrete surfaces, lamination of fiber to be made on wooden surfaces or similar bonding processes

Type	TS EN 1504-2/ April 2008 Principle 5 (PR): 5 1 Physical Resistance / Surface Improvement Coating Application (C)
Colour	Colourless
Outlook	Transparent
Solid Matter by Weight, %	38
Density	0,96 g/cm³
Waste	0,150–0,400 kg/m2 (Variable depending on surface suction power)
Package	17,5 kg Component + 2,5 kg B Component = Total 20 kg
Flash Point	>25 °C
Mixture Ratio	7 /1
Application Methods	Brush, Roller, Air Gun, Airless Gun
Mixture Life	4 hours / 25 °C
Shelf Life	1 year
Waiting Time Between Coats	12 hours / 25 °C
Drying Time	12 hours / 25 °C
Mechanical Strength	7 days
Equipment Cleaning	Epoxy Thinner

SURFACE PREPARATION

*The free particles on the surface should be completely cleaned and mechanically the surfaces should be roughened with sandpaper and cleaned from dust.

MIXING PREPARATION

A and B component should be mixed with a low speed mixer for at least 3-4 minutes until a homogenous mixture is obtained by paying attention to mixture ratios. It is ready for application after mixing.

APPLICATION CONDITIONS

* Surface should have sufficient strength.

* The surface must be clean and dry. Humidity must not exceed 5%.

* The SC 092 Epoxy adhesion bridge must have been completed ıts curing before the top coat is applied.

* Avoid application in very humid environments and below 5°C.

* Mixing ratios should be considered.