EPOXY PRODUCTS
-
Floor Coatings
- PRIMER WG 032
- WALL WG 034
- BRV SC 105
- BRV SC-200 K
- PRIMER SC 210
- PRIMER SC 215
- PRIMER SC 220
- SC Z-230 Self Leveling C Komponent
- PRIMER SC 270
- PRIMER SC 325
- DECOFLOOR SC 330
- FLOOR SC 470
- SC 600
- WALL SC 605
- WALL SC 605-C
- BRV SC 610 • Solvent-Free Epoxy Topcoat
- BRV SC 620 • Solvent-Free Textured Epoxy Topcoat
- BRV SC 625 SOLVENT-FREE EPOXY TOP COAT NON-SLIP FLOOR PAINT
- FLOOR SC 645
- SC 650 ST
- FLOOR SC 902
- FLOOR SC 903
- BRV SC 905 • CHEMICAL RESISTANT SOLVENT-FREE EPOXY TOP COAT FOR VERTICAL SURFACES
- FLOOR SC 950
- FLOOR SC 1200
- FLOOR AC 6380
- ROAD AC 6388
- Waterproofing Products
- Repair Anchorage and Assembly Products
- Joint Filler and Ceramic Adhesive Products
- Wood Protection Adhesive and Lamination Products
- Natural Stone Protectors
- Water Reservoir & Drainpipe Insulation Products
- Anticorrosive Products For Metal Surfaces
- Thinners
-
Floor Coatings
-
POLYURETHANE PRODUCTS
- FLOOR COVERING AND PAINTING PRODUCTS
- WATERPROOFING PRODUCTS
- STRUCTURAL REINFORCEMENT REPAIR ANCHOR INSTALLATION PRODUCTS
- WOOD PROTECTOR, ADHESIVE AND LAMINATION PRODUCTS
- NATURAL STONE PROTECTIVE PRODUCTS
- ANTICORROSIVE PRODUCTS FOR METAL SURFACES
- CONCRETE SURFACE PROTECTION AND POLISHING PRODUCTS
- THINNERS
-
ACRYLIC PRODUCTS
- WATERPROOFING PRODUCTS
- FLOORING AND PAINTING PRODUCTS
- INTERIOR AND EXTERIOR INSULATION & PAINT PRODUCTS
- SPECIAL FLAME RETARDANT INSULATION PRODUCTS
FLOOR PU 145
DEFINITION
USAGE AREAS
It is used as elastic polyurethane floor covering at hospitals, schools, offices, sports halls, shopping centers, hotels, storage areas, cold storage, in the frigofric vehicle chassis, in food production facilities and in all industrial areas where hygiene is required..
Type | TS EN 1504-2/ April 2008 Principle 5 (PR): 5.1 Physical Resistance / Surface Improvement Coating Application (C) |
| Colour | RAL colours |
| Outlook | Semi Bright There may be discoloration in environments exposed to direct sunlight, but it does not negatively affect the performance of the product. |
| Solid Matter by Weight, % | 100 |
| Density | A+B 1,20 gr/cm³ A+B+C 1,40 gr/cm³ |
| Waste | For 1 mm dry film thickness A+B 1,200 kg / m² For 1 mm dry film thickness A+B+C 1,400 kg/m² |
| Package | Component A:16 kg Component B:4 kg Total: 20 kg Component A:16 kg Component B: 4 kg Component C:12,5 kg Total.32,5 kg Component C is in 25 kg Kraft Bag packaging |
Flash Point | >25 °C |
Mixture Ratio | 4 / 1 |
Application Methods | Brush, Roller, Trowel |
Mixture Life | 30 minutes /25 °C |
Shelf Life | 1 year |
Waiting Time Between Coats | 8 hours/25 °C |
Drying Time | 8 hours/25 °C |
Mechanical Strength | 7 days |
Shore A Hardness (7 days / 25°C) Wear Resistance (TABER) | 75 223 mg TS 8103 EN ISO 5470-1:2002 0,001 (kg/m².h ) TS EN 1062-3:2008 Sınıf ll TS EN ISO 6272-1:2006 5 (N/mm²) TS EN 1542:2001 Efl |
Equipment Cleaning | Polyurethane Thinner |
* Prior to applying the primer coat, the surfaces to be applied must be free from oil, dust, and dirty.
* Free parts on the surface, cement grout on concrete surfaces and parts that prevent adhesion must be cleaned.
MIXING PREPARATION
A and B component should be mixed with a low speed mixer for at least 3-4 minutes until a homogenous mixture is obtained by paying attention to mixture ratios. It is ready for application after mixing. The mixture should be consumed within 25-30 minutes.