FLOOR SC 1200 • Epoxy Floor Coating for Refrigerated Vehicle Containers
Two-Component, Solvent-Free Epoxy Refrigerated Vehicle Container Floor Coating
Product Description:
This two-component, solvent-free epoxy coating is a high-performance floor coating system specifically developed for refrigerated vehicle bodies and modular container floors. Thanks to its high water resistance and waterproof structure, it provides long-lasting protection in humid and frequently washed environments. Its antibacterial properties make it safe to use in areas where hygiene standards are critical.
Its special formula provides strong adhesion to metal, OSB, and fiber cement surfaces, ensuring high performance on various floor types. After completing its chemical reaction, it forms a dense, compact, and 100% hygienic layer on the surface. Its high mechanical strength and abrasion resistance make it resistant to forklift traffic and prevent deformation under heavy loads.
Its solvent-free composition ensures safety for the environment and user health, offering low odor and comfortable working conditions during application.
Areas of application:
- Refrigerated vehicle bodies
- Modular container floors
- Transportation and storage areas requiring hygiene
- Metal, OSB and fiber cement surfaces
- Floors exposed to forklift traffic
Key Features:
- High water resistance and waterproof structure
- Antibacterial and hygienic surface
- High mechanical strength resistant to forklift traffic
- Strong adhesion to metal, OSB and fiber cement surfaces
- Solvent-free and environmentally friendly formula
- Resistant to abrasion and heavy use
|
Type |
TS EN 1504-2 / April 2008 Principle 5 (PR): 5,1 Physical Resistance / Surface Improvement Coating Application ( C ) |
|
Colour |
RAL colours |
|
Outlook |
Bright |
|
Solid Matter by Weight, % |
100 |
|
Density |
1,70 g/cm³ |
|
Waste |
0,800-1,600 kg/m² |
|
Package |
20 kg A Component+ 5 kg B Component: Total 25 kg |
|
Flash Point |
>25 °C |
|
Mixture Ratio |
4 / 1 |
|
Application Methods |
Trowel |
|
Mixture Life |
30 minutes / 25°C |
|
Shelf Life |
1 year |
|
Waiting Time Between Coats |
12 hours / 25°C |
|
Drying Time |
12 hours / 25°C |
|
Mechanical Strength |
7 days |
|
Equipment Cleaning |
Epoxy Thinner |
SURFACE PREPARATION
* The surfaces to be applied must be free from oil, dust, and dirty.
* Free parts on the surface, cement grout on concrete surfaces and parts that prevent adhesion must be cleaned.
MIXING PREPARATION
A and B component should be mixed with a low speed mixer for at least 3-4 minutes until a homogenous mixture is obtained by paying attention to mixture ratios. It is ready for application after mixing.
COATING SYSTEM
If the floor is precast concrete panel, depending on the surface suction power, the SC 200-K Condensed Intermediate Primer is applied at 0.300-0.800 kg /m². If the floor is sheet metal, anticorrosive primer must be used. The minimum dry film thickness of these primers should be 100 microns. Also, the cleaning of the sheets must be at SA 2½ ranks
APPLICATION CONDITIONS
* Surface should have sufficient strength
* The surface must be clean and dry. Humidity must not exceed 5%, If the humidity is above this ratio, SC 220 100% Epoxy Primer for humid surfaces used on humid surfaces should be preferred.
* Surface should have sufficient strength
* The surface must be clean and dry. Humidity must not exceed 5%, If the humidity is above this ratio, SC 220 100% Epoxy Primer for humid surfaces used on humid surfaces should be preferred.
* The primer to be used must have been completed its curing before the top coat coating is started.
* Avoid application in very humid environments and below 10°C.
* Mixing ratios should be considered.
Products that can be used under this product:
* SC 210 Multipurpose Epoxy Primer
* SC 200-K Condensed Intermediate Coat Primer
* SC 220 Epoxy Primer for 100% Humidy Surfaces
* SC 270 Epoxy Impregnating Primer with Low Viscosity
* AC 2480 Epoxy Intermediate Coat Primer
* AC 070 Epoxy Zinc Rich Primer