WALL PU 125
DEFINITION
Aliphatic polyurethane top layer paint with two components and low amount of solvent and high UV endurance.
USAGE AREAS
It is used as an acrylic polyurethane based paint with high mechanical endurance and wear resistance, easy to clean and used in concrete floors and surfaces of factories inside and outside, assembly workshops, depots, aircraft hangers, shopping centers, food facilities, water tanks, hospitals, chemical and drug industry, energy power plants and many others additionally in closed and open auto-parks, bicycle paths, setting road lines of all industrial floors and drawing of special lines.
|
Tipi |
TS EN 1504-2/April 2008 Principle 5(PR): 5.1 Physical Resistance / Surface Improvement coating Application C |
||
|
Color |
RAL colors |
||
|
Appearance |
Semi Matt |
||
|
Thinner |
Polyurethane Thinner |
||
|
Solid Matter By Weight, % |
70 |
||
|
Density |
1,30 g/cm³ |
||
|
Waste |
50-100 gr / m2 |
||
|
Package |
18 kg A Component+ 2 kg B Component: Total 20 kg |
||
|
Flash Point |
>25 °C |
||
|
Mixing Ratio |
9/1 |
||
|
Application Methods |
Brush, Roller, Air Gun, Airless Gun |
||
|
Mixture Life |
1 hour/25 °C |
||
|
Shelf Life |
1 year |
||
|
Waiting Time Between Coating |
4 hours/25 °C |
||
|
Drying Time |
4 hours/25 °C |
||
|
Mechanical Strength |
7 days |
||
|
Equipment Cleaning |
Polyurethane Thinner |
||
SURFACE PREPARATION
Prior to the implementation of prime layer, the free particles, residual paint, oil, dirt, and dust on the surface should be totallycleared, broken parts and cracks should be repaired and the surface should definitely be roughened before application.
MIXTURE PREPARATION
The components A and B should be mixed for at least 3-4 minutes with the aid of a low speed mixer until a homogeneous mixture is obtained, taking into account the mixing ratios. It is ready for application after mixing
APPLICATION CONDITIONS
* Application should not be done if the application environment and the surface temperature is under +10 ºC or over +30 ºC
* Application should be avoided when there is precipitation and wind.
* After the completion of painting, it should be protected from contact with water at least for 24 hours.
* Relative humidity must not exceed 70% during application.
Products that could be used under this product :
*AC 2480 Epoxy Middle Layer Prime