FLOOR SC 645 • Epoxy-Based Orange Peel Patterned Top Coating
Two-component, solvent-free orange peel pattern epoxy topcoat.
Public Works Item No: 04.379/H04
Product Description:
This two-component, solvent-free epoxy resin-based topcoat is a high-performance product developed for industrial floors. Its orange peel texture provides slip resistance and an aesthetically pleasing appearance. It boasts high mechanical strength and abrasion resistance, offering long-lasting durability in high-traffic and heavy-load areas. Its stain-resistant formula is resistant to harsh substances such as tea, coffee, ketchup, salt water, soapy water, engine and hydraulic oil, 20% caustic soda solution, and 10% acetic acid solution. Its easy-to-clean and hygienic properties make it particularly suitable for food processing facilities, hospitals, and areas where hygiene is critical.
Areas of application:
This orange peel patterned epoxy topcoat can be safely used in industrial areas such as parking lots, shops, factories, assembly plants, warehouses, aircraft hangars, food facilities, hospitals, chemical and pharmaceutical industries, and power plants. Its mechanical durability and stain-resistant properties make it suitable for heavy use, providing both hygienic and aesthetically pleasing floor covering.
Key Features:
- Orange peel pattern surface for non-slip and aesthetic appearance
- High mechanical strength and abrasion resistance
- Stain-resistant formula (tea, coffee, ketchup, salt water, soapy water, engine and hydraulic oil, 20% caustic soda, 10% acetic acid)
- Easy to clean and hygienic
- Safe and durable use on all industrial floors
- Environmentally and user-friendly with solvent-free formula
| Type | TS EN 1504-2/ April 2008 Principle 5 (PR): 5 1 Physical Resistance / Surface Improvement Coating Application (C) |
| Colour | RAL colours |
| Outlook | Semi-matt |
| Solid Matter by Weight, % | 98 |
| Density | 1,58 g/cm³ |
| Waste | Intermediate Coat Coating: 0,400-0,500 kg / m2 Textured Top Coat Coating: 0,500-0,600 kg/ m2 |
| Package | 22,50 kg A Component + 2,50 kg B Component : Total 25 kg |
| Flash Point | >25 °C |
| Mixture Ratio | 9 / 1 |
| Application Methods | Intermediate Coat Coating: Roll,Trowel Textured Top Coat Coating: Mop, Trowel (For spreading to the surface) Epoxy Roll (for grinding), Textured Roll (For Textured Pattern) |
| Mixture Life | 20 minutes / 25°C |
| Shelf Life | 1 year |
| Waiting Time Between Coats | 12 hours / 25°C |
| Drying Time | 12 hours / 25°C |
| Mechanical Strength | 7 days |
| Shore D Hardness (EN ISO 1542) Adhesion Strength (TS EN ISO1542) Pressure Resistance (TS EN 12190 ) Bending Strength ( TS EN 12190 ) Tensile strength (DIN 53504) Fire Reaction Class |
75 (7 days / 25°C) >2 N / mm² 80 N/ mm² 45 N/ mm² 20 N/ mm² Cfl |
| Equipment Cleaning | Epoxy Thinner |
SURFACE PREPARATION
* The surfaces to be applied must be free from oil, dust, and dirty.
* Free parts on the surface, cement grout on concrete surfaces and parts that prevent adhesion must be cleaned.
MIXING PREPARATION
A and B component should be mixed with a low speed mixer for at least 3-4 minutes until a homogenous mixture is obtained by paying attention to mixture ratios. It is ready for application after mixing.
COATING SYSTEM
After finishing the priming process, SC 645 and 0,400-0,500 kg/m² waste is applied as interlayer application with roll or trowell. After 12 hours at 25°C the final coat is applied. The final layer application is spread by using a crestless trowel or mop until a homogeneous thickness is obtained with 0,500-0,600 kg/m² waste, It is polished over with an epoxy roll and patterned with textured roll. To make a faultless coating, a textured roll must be applied in the same direction. Cross application should be avoided. It is recommended to apply PU 125 protective coating with 0,150-0,200 kg/m² waste where high UV resistance is desired
APPLICATION CONDITIONS
* Surface should have sufficient strength. The concrete has a compression strength of at least 25 N/mm², nd a tensile strength of at least 1,5-2 N/mm².
* The surface must be clean and dry. Humidity must not exceed 5%, If the humidity is above this ratio, SC 220 100% Epoxy Primer for humid surfaces used on humid surfaces should be preferred.
* Avoid application in very humid environments and below 10°C.
* Mixing ratios should be considered.
Products that can be used under this product:
* SC 210 Multipurpose Epoxy Primer
* SC 215 Solvent Free Epoxy Primer
* SC 220 Epoxy Primer for 100% Humidy Surfaces
* SC 270 Epoxy Impregnating Primer with Low Viscosity
* SC 200 K Self Leveling Intermediate Coat Primer