BRV SC 605 • Solvent-Free Epoxy Topcoat Paint for Vertical Surfaces
Two-Component, Solvent-Free TIX Epoxy Topcoat Paint – For Vertical Surfaces
Product Description:
This two-component, solvent-free TIX epoxy topcoat paint is designed to provide high performance and durability, especially on vertical surfaces. With its high mechanical strength and abrasion resistance, it offers long-lasting protection in industrial settings. Its solvent-free formula makes it environmentally and user-friendly. The product exhibits excellent adhesion to rough or plastered surfaces and offers easy cleanability for hygienic areas. Its anti-corrosion properties make it suitable for safe use on metal structures, bridge girders, pipelines, and nuclear waste storage containers.
Areas of application:
This TIX epoxy topcoat paint can be used in all industrial environments where hygiene and durability are important, such as factories and assembly plants, warehouses, aircraft hangars, shops, parking lots, food facilities, hospitals, the pharmaceutical and chemical industries, and nuclear power plants and radiochemical production areas. It provides superior performance on concrete and metal surfaces, plastered areas, water tanks, and structures requiring anti-corrosion protection.
Key Features:
- Special TIX formula for vertical surfaces
- High mechanical strength and abrasion resistance
- Easy to clean and hygienic
- Excellent adhesion to concrete, metal and plaster-treated surfaces
- Anti-corrosion protection and solvent-free, environmentally friendly formula
- Ideal for industrial, hygienic and controlled areas
|
Type |
TS EN 1504-2/ April 2008 Principle 5(PR): 5,1 Physical Resistance / Surface Improvement Coating Application ( C ) |
|
Color |
RAL colors |
|
Appearance |
Bright |
|
Solid Matter By Weight, % |
95 |
|
Density |
1,55 g/cm³ |
|
Waste |
0,200-0,500 kg/m² |
|
Package |
20 kg A Component + 4 kg B Component: Total 24 kg |
|
Flash Point |
>25 °C |
|
Mixture Ratio |
5 / 1 |
|
Application Methods |
Brush, Roller, Airless Gun, |
|
Mixture Life |
30 minutes/ 25°C |
|
Shelf Life |
1 year |
|
Waiting Time Between Coating |
12 hours/ 25°C |
|
Drying Time |
12 hours / 25°C |
|
Mechanical strength |
7 days |
|
Shore D Hardness Fire Reaction Class |
70 (7 days / 25°C) C |
|
Equipment Cleaning |
Epoxy Thinner |
SURFACE PREPARATION
* The surfaces to be applied should be clear of grease, dust and dirt.
* Free particles on surfaces, cement slurry on cement surfaces and parts that prevent gluing should be cleared.
* Yüzeydeki serbest parçalar, beton yüzeylerdeki çimento şerbeti ve
yapışmaya engel olan parçalar temizlenmelidir.
MIXTURE PREPARATION
The components A and B should be mixed for at least 3-4 minutes with the aid of a low speed mixer until a homogeneous mixture is obtained, taking into account the mixing ratios. It is ready for application after mixing
COATING SYSTEM
The concrete surface where application would be done should be primed using SC 210 multi-purpose Epoxy Primer, SC 215 Epoxy Primer without Solvent or SC 270 Low Viscosity Epoxy Impregnated Primer. On moist surfaces SC 220 should be used and on 100% moist surfaces Epoxy Primer. 12 hours after the priming process, epoxy painting process can start. In brush or roller applications, epoxy brush or roller should be used. If it is necessary, the product itself can also be used as the first layer primer. In applications over plaster, prior to using SC 605 Epoxy Top Layer Pint without solvent, water based acrylic BRV Primer 405 should be applied as transition primer. In cases where high UV durability is desired, it is suggested to apply P125 protective coating with 0,150 – 0,200 kg/m² waste.
APPLICATION CONDITIONS
* The surfaces must have sufficient endurance. Concrete should endure minimum 25 N/mm² pressure and endure against at least 1,5-2 N/mm² pull-off strength.
* The surface should be clean, straight, dry and should not exceed 5% moisture and if moisture is above this rate, SC 220 should be used on moist surfaces and Epoxy Primer on 100% moist surfaces.
* The priming should have completed its curing prior to moving on to the top layer epoxy painting process.
* Application should be avoided under 10°C and in high moisture environments.
* The mixture ratios should be paid attention to.
Products suggested to be used under this product :
* SC 210 Multi-purpose Epoxy Primer <p<* 100%=”” 220=”” <p=”” epoxy=”” for=”” moist=”” primer=”” sc=”” surfaces=””>* SC 270 Epoxy adhesion bridge Low Viscosity Impregnated Primer</p<*>